Sample ID | Substrate | Implantation conditions | Laser spot | Spot size | PLM conditions | Good/Bad | Characterization | Notes | Current location | Owner |
---|---|---|---|---|---|---|---|---|---|---|
n-Si(100), P doped | Au, 50 keV, 1e14 /cm2 |
|
|
|
|
|
|
|
| |
|
|
| A | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| MIT | Jonathan |
|
|
| B | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| MIT | Jonathan |
|
|
| C | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| MIT | Jonathan |
|
|
| D | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
| Raman |
| Benet | Jay |
|
|
| E | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| Benet | Jay |
n-Si(100), P doped | Au, 50 keV, 5e14 /cm2 |
|
|
|
|
|
|
|
| |
|
|
| A | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Good |
|
| MIT | Jonathan |
|
|
| B | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Bad | SEM, EBSD, TEM | Single Crystal | MIT | Jonathan |
|
|
| C | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Good |
|
| MIT | Jonathan |
|
|
| D | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
| Raman |
| Benet | Jay |
|
|
| E | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| Benet | Jay |
p-Si(111), B doped | Au, 50 keV, 1e14 /cm2 |
|
|
|
|
|
|
|
| |
|
|
| A | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Bad | SEM, EBSD, TEM | Stacking Faults | MIT | Jonathan |
|
|
| B | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Bad |
|
| MIT | Jonathan |
|
|
| C | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Good |
|
| MIT | Jonathan |
|
|
| D | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 | Good |
|
| MIT | Jonathan |
|
|
| E | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
| Raman |
| Benet | Jay |
|
|
| F | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| Benet | Jay |
p-Si(111), B doped | Au, 50 keV, 5e14 /cm2 |
|
|
|
|
|
|
|
| |
|
|
| A | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
| SEM, EBSD | Stacking Faults | MIT | Jonathan |
|
|
| B | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| MIT | Jonathan |
|
|
| C | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
| Raman |
| Benet | Jay |
|
|
| D | 2.5 x 2.5 mm2, masked | Harvard YAG355, 1 shot, 0.7 J/cm2 |
|
|
| Benet | Jay |
n-Si(100), P doped | ||||||||||
Au, 50 keV, 1e15 /cm2 |
|
|
|
|
|
|
|
| ||
|
|
| A | 2.5 x 2.5 mm2, masked | Benet YAG355, 1 shot, 0.65 J/cm2 |
| SEM | Good | Harvard | Austin |
|
|
| B | 2.5 x 2.5 mm2, masked | Benet YAG355, 1 shot, 0.65 J/cm2 |
| SEM | Good | Harvard | Austin |
|
|
|
|
|
|
|
|
|
|
|