Sample Master List
Sample ID |
Substrate |
Implantation conditions |
Laser spot |
Spot size |
PLM conditions |
Good/Bad |
Characterization |
Notes |
Current location |
Owner |
|---|---|---|---|---|---|---|---|---|---|---|
1 |
n-Si(100), ρ = 1-10 Ω-cm |
Au, 80 keV, 1e15 /cm2 |
|
|
|
|
|
|
|
|
|
|
|
A |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
MIT |
Jonathon |
|
|
|
B |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
MIT |
Jonathon |
|
|
|
C |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
MIT |
Jonathon |
|
|
|
D |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
|
|
|
E |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
2 |
n-Si(100), ρ = 1-10 Ω-cm |
Au, 80 keV, 5e15 /cm2 |
|
|
|
|
|
|
|
|
|
|
|
A |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Harvard |
Austin |
|
|
|
B |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Harvard |
Austin |
|
|
|
C |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Harvard |
Austin |
|
|
|
D |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
|
|
|
E |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
p-Si(111), ρ = 1000 Ω-cm |
Au, 80 keV, 1e15 /cm2 |
|
|
|
|
|
|
|
|
|
|
|
|
A |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
Bad |
SEM, EBSD, TEM |
Stacking Faults |
MIT |
Jonathon |
|
|
|
B |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
Bad |
|
|
MIT |
Jonathon |
|
|
|
C |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
Good |
|
|
MIT |
Jonathon |
|
|
|
D |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
Good |
|
|
MIT |
Jonathon |
|
|
|
E |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
|
|
|
F |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
p-Si(111), ρ = 1000 Ω-cm |
Au, 80 keV, 5e15 /cm2 |
|
|
|
|
|
|
|
|
|
|
|
|
A |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
MIT |
Jonathon |
|
|
|
B |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
MIT |
Jonathon |
|
|
|
C |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
|
|
|
D |
2.5 x 2.5 mm2, masked |
Harvard YAG, 1 shot, 0.7 J/cm2 |
|
|
|
Benet |
Jay |
|
|
|
|
|
|
|
|
|
|
|